产品描述：

Description
Denso Protal 7200 is a VOC free, 100% solids epoxy coating specially formulated to compliment FBE coated pipe. It is a high build liquid coating that is brush or spray applied in one coat in the field or shop. It cures very fast to allow quick handling and backfill times.
Uses
On-site protection of girth welds, tie-ins, welds for boring applications, repairs to FBE, push-back applications, station piping, fittings and fabrication. Also used for main line pipe coating, sacrificial coating for directional drill and road bore pipe, and rehabilitation of existing pipelines.
Features
• Fast touch dry and set times
• High temperature resistance (up to 185°F)
• High build (up to 50 mils in one coat)
• Excellent adhesion (complements FBE coated pipe)
• High abrasion resistance for drilling applications
• Safe and environmentally friendly
• Does not shield cathodic protection
• Can be applied with brush, roller or spray
• Available in a variety of packaging options
Application,
Brush
Prepare surfaces by grit blasting to a clean near white finish, SSC-SP 10/ NACE No. 2. Initially stir the base and hardener. Add the hardener to base and mix until a constant color is achieved making sure all sides of container are scraped. Pour mixed material onto surface and brush, trowel or roll to required mil thickness. A wet film thickness gauge shall be used to measure mil thickness. If surface temperature falls below 50°F (10°C), surface must be preheated to achieve cure. Preheat may be achieved with a propane torch or induction coil. Resin and hardener component shall be kept warm, at a minimum of 68°F (20°C), to mix easily.
Application,
Spray
Prepare surfaces by grit blasting to a clean near white finish, SSC-SP 10/ NACE No. 2. The equipment should be a plural component airless spray unit with a proportioning pump capable of a volume mixing ratio of 3:1. Standard ancillary equipment should include minimum 10 gallon hoppers, static mixers, whip hose, and mastic gun. (Applicator should consult with Denso regarding recommended equipment). A wet on wet spray technique should be used to achieve a minimum thickness of 20 mils. The coating thickness should be measured using a wet film thickness gauge.
Packaging
1 liter kit and 90 liter drums standard. Other kit sizes are available. Dual cartridge repair tubes (375 ml & 50 ml) and dispensing guns available for small repair areas.
Storage
Minimum 24 months when stored in original containers @ 41°F (5°C) to 100°F (36°C). On job site where temperatures are below 68°F (20°C) product must be kept warm to mix properly.
Cleaning
Clean equipment with solvent cleaner (xylene 95%, butanol 5%).
Safety
Spray or brush under well ventilated conditions. Wear suitable protective clothing and glasses. See:
MSDS for Protal 7200 "A"
MSDS for Protal 7200 "B"
 
Technical Data
Properties
Data
Solids Content
100%
Base Component - unmixed at 77°F (25°C)
     Specific Gravity
     Viscosity
     Color

1.68
Soft gel
White
Hardener - unmixed at 77°F (25°C)
     Specific Gravity
     Viscosity
     Color

1.04
Liquid (400 cps)
Forest green
Mixed Material - mixed at 77°F (25°C)
     Specific Gravity
     Viscosity
     Color

1.53
Light gel
Forest green
Mixing Ratio
     By Volume

3 parts base, 1 part hardener
Cure Times
     Pot Life @ 77°F (25°C)
     Handling Time @ 77°F (25°C)

6 to 8 minutes
60 to 90 minutes
Theoretical Coverage
14 ft2 (1.3 m2) / liter
Thickness
     Minimum
     Recommended
  
20 mils
25-30 mils
Holiday Detection
2,000 volts maximum
Cathodic Disbondment Test
     28 Days @ 77°F (25°C)
     28 Days @ 150°F (65°C)
     28 Days @ 175°F (80°C)

3 mm
4 mm
7 mm
Hardness
Shore D 85 ± 2
Impact Resistance
Excellent
Application & Service Temperature
-30°F (-34°C) to 185°F (85°C).
Note: If temperature falls below 50°F (10°C),
surface must be preheated.
Glass Transition
185°F (85°C)
Impact Resistance
Excellent
 